Hybrid dielectric film for high temperature application

ABSTRACT

A high-temperature insulation assembly for use in high-temperature electrical machines and a method for forming a high-temperature insulation assembly for insulating conducting material in a high-temperature electrical machine. The assembly includes a polymeric film and at least one ceramic coating disposed on the polymeric film. The polymeric film is disposed over conductive wiring or used as a conductor winding insulator for phase separation and slot liner.

BACKGROUND

The disclosure relates generally to an assembly having, and a methodproviding, improvement in thermal oxidation and corona dischargeresistance, and more particularly to an assembly and a method forforming a flexible high heat resistant dielectric material.

Polymeric films are known to have utility as insulating materials inmotors and generators. Known polymeric films serve as dielectricmaterials insulating conducting materials from other conductingmaterials to inhibit shorting, or short circuiting, of an electricalconnection. Insulation provides protection against voltage hazards andinhibits leakage of current as well as electric discharge and shortcircuits.

FIG. 1 illustrates schematically a section of a motor 10. Polymericfilms are used as insulating materials in various locations. Forexample, polymeric films are used as phase insulation/end windinginsulation 12. Also, polymeric films are used as ground insulation/slotliners 14. Polymeric films can also be used as turn insulation 16, acopper wire coating. Wound wires 18, 20 and 22 are positioned relativeto a voltage stress level in the motor 10. For an AC motor or generator,usually there are three voltage phases, 120 degree apart. Wound wire 18generally refers to wires next to each other in two different phases,where it has the highest voltage drop, so insulator in addition to wirecoating is needed to separate these phase-to-phase voltage drops. Thewound wire 20 generally refers to a wire next to the steel core (orsteel laminates) which is grounded. The voltage between the wire 20 andthe core is the line voltage to ground which is also high, so groundinsulation in addition to wire coating is needed. Wound wire 22 refersto wires next to each other in the same voltage phase, where the voltagedrop is the least, so the coating on the conductive wire may providesufficient insulation.

The polymeric films that are currently used in motors and generators areformed of one or more of cross-linked polyethylene, polypropylene,polyester, polycarbonate, polyurethane, polyphenylene oxide, high heatpolymer films such as polyimide, aromatic polyimide, aromatic polyester,polyetherimide, polyamideimide, polyphenylene sulfide, polyphenylenesulfone, polyetheretherketone (PEEK), polytetrafluoroethylene (PTFE) andother fluoropolymers.

Film-like material is often used with conducting materials like wiresused in electrical machines because such material lends flexibility.Flexibility is needed in that the conducting materials often are woundor are maintained in curved and/or non-planar orientations. To properlycoat such conducting materials without creating undue stress on theconducting materials, thin film-like materials are used. Film-likematerials are also frequently used as phase separation and slot linersfor winding wires. Flexibility and abrasion resistance of films areneeded for them to survive the mechanical stress during manufacturingassembly processes.

However, disadvantages exist in known polymeric films used to insulateconducting materials within motors and/or generators. Currently knownpolymeric films have heat stability or thermal index only up to 260° C.What is meant by “heat stability” or “thermal index” is that thematerial's dielectric and/or mechanical integrity is intact after 20,000hours of thermal aging at 260° C. The standard test method used fordefining thermal index can be found in ASTM D2307. Newer motors andgenerators require materials which can withstand higher heat than 260°C., and therefore often are manufactured to operate at highertemperatures.

Previous generation electric drives mostly operated with line voltageoperated at a constant frequency unlike newer pulse-width modulated(PWM) driven motor/drives driven by high dV/dT PWM drives and operatednear or higher than Partial Discharge Inception Voltages (PDIV) orcorona inception voltage (CIV).

In addition, limited volume/space limits the separation and spacing ofhigh voltage signals/power lines in electric machine windings as well ascabling and power electronics combined with low pressure with hightemperature often results in the operation near or higher than PDIV/CIVfor electric discharge.

Where polymeric film is used in high temperature applications, mica,ceramic and glass tape have been traditionally employed to providegreater heat resistance. However, because of their rigidity and lowdielectric strength, high thickness is required to achieve properdielectric strength. The size and weight of power units utilizing thesetypes of insulation tends to be large and heavy, respectively, and thuspower density of the system as a whole is sacrificed.

Another disadvantage is that known polymeric films can only withstandcorona discharges for a limited period of time. For example, in anexperiment run by the inventors a polyimide film was exposed to a 20kilohertz (kHz) continuous square wave pulse. The polyimide film lastedless than 10 minutes without degrading to the point of breaking down, orshort circuiting.

Given the known disadvantages of the current state of the art ofinsulating films, an improved insulation assembly and method forinsulating conducting materials in an electrical machine would bewelcome in the art.

SUMMARY

An embodiment of the disclosure includes a high-temperature insulationassembly for use in high-temperature electrical machines. The assemblyincludes a polymeric film and at least one ceramic coating disposed onthe polymeric film. The polymeric film is disposed either overconductive wiring or used as conductor winding insulator.

Another embodiment of the disclosure includes an electrical machine thatincludes a motor or generator comprising conductive wiring wound innon-planar orientations and an insulation assembly for insulating theconductive wiring. The insulation assembly includes a polymeric film andat least one ceramic coating disposed on the polymeric film. Thepolymeric film is disposed over the conductive wiring or used forconductor winding insulator.

One embodiment includes a method for forming a high-temperatureinsulation assembly for insulating conducting material in ahigh-temperature electrical machine. The method includes depositing atleast one layer of a ceramic material on a polymeric film and disposingthe at least one layer of a ceramic material and the polymeric filmadjacent to a conducting material.

These and other features, aspects and advantages may be furtherunderstood and/or illustrated when the following detailed description isconsidered along with the attached drawings.

DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic depiction of a section of a motor showing variouslocations where insulation is used.

FIG. 2 is a schematic depiction of an insulation assembly in accordancewith an embodiment.

FIG. 3 is a schematic depiction of a ceramic coating in accordance withan embodiment.

FIG. 4 is a transmission electron microscopy image depicting aninsulation assembly in accordance with an embodiment.

FIG. 5 is a schematic depiction of a deposition system for forming aninsulation assembly in accordance with an embodiment.

FIG. 6 is a schematic depiction of a deposition system for forming aninsulation assembly in accordance with an embodiment.

FIG. 7 is a graphical representation exhibiting the thermal stability ofa known insulation assembly and insulation assemblies formed inaccordance with an embodiment, plotting loss of weight in percentageagainst temperature for a temperature increase rate of 10° C./minute.

FIG. 8 depicts process steps for forming an insulation assembly about aconducting material in accordance with an embodiment.

DETAILED DESCRIPTION

The present specification provides certain definitions and methods tobetter define the embodiments and aspects of the system/method and toguide those of ordinary skill in the art in the practice of itsfabrication. Provision, or lack of the provision, of a definition for aparticular term or phrase is not meant to imply any particularimportance, or lack thereof; rather, and unless otherwise noted, termsare to be understood according to conventional usage by those ofordinary skill in the relevant art.

Unless defined otherwise, technical and scientific terms used hereinhave the same meaning as is commonly understood by one of skill in theart to which this invention belongs. The terms “first”, “second”, andthe like, as used herein do not denote any order, quantity, orimportance, but rather are used to distinguish one element from another.Also, the terms “a” and “an” do not denote a limitation of quantity, butrather denote the presence of at least one of the referenced item, andthe terms “front”, “back”, “bottom”, and/or “top”, unless otherwisenoted, are merely used for convenience of description, and are notlimited to any one position or spatial orientation.

The modifier “about” used in connection with a quantity is inclusive ofthe stated value and has the meaning dictated by the context (e.g.,includes the degree of error associated with measurement of theparticular quantity). Reference throughout the specification to “oneembodiment”, “another embodiment”, “an embodiment”, and so forth, meansthat a particular element (e.g., feature, structure, and/orcharacteristic) described in connection with the embodiment is includedin at least one embodiment described herein, and may or may not bepresent in other embodiments. In addition, it is to be understood thatthe described inventive features may be combined in any suitable mannerin the various embodiments.

As illustrated in FIG. 2, there is shown therein an insulation separatorassembly 100. The insulation separator 100 includes a polymeric film 102sandwiched between first and second ceramic coatings 104 a, 104 b.

The polymeric film 102 may be formed of one or more of cross-linkedpolyethylene, polypropylene, polyester, polycarbonate, polyurethane,high heat polymer films such as polyimide, aromatic polyimide, aromaticpolyester, polyetherimide, polyamideimide, polyetheretherketone (PEEK),and polytetrafluoroethylene (PTFE). Alternatively, the polymeric film102 may be formed of any number of other suitable materials, such as,for example, polyphenylene oxide, polyphenylene sulfone, polyethersulfone, polyphenylene sulfide, or other suitable fluoropolymers such asperfluoroalkoxy (PFA), polyvinylidene fluoride (PVDF),fluoroethylene-propylene (FEP), ethylene-tetrafluoroethylene copolymer(ECTFE), and polychlorotrifluoroethylene (PCTFE) to name a few.

Each of the ceramic coatings 104 a, 104 b may be formed of a singlelayer or of many layers of the coatings. Further, the ceramic coatings104 a, 104 b both may, instead of sandwiching polymeric film 102, be onone side of the polymeric film. The ceramic coatings 104 a, 104 b eachmay be formed of one or more inorganic materials. More specifically, theceramic coatings 104 a, 104 b each may be formed of silicon nitride;silicon oxide; silicon oxynitride; aluminum oxide; zirconium oxide;combinations of elements of Groups IIA, IIIA, IVA, VA, VIA, VIIA, IB,and IIB; metals of Groups IIIB, IVB, and VB; rare-earth metals; and, anycombinations thereof.

Alternatively, the ceramic coatings 104 a, 104 b each may be formed ofone or more organic materials. More specifically, the ceramic coatings104 a, 104 b each may be formed of silicon carbide, organometallicsilanes, or forms of ceramic coating after sintering.

The ceramic coating 104 a may be formed of different materials than theceramic coating 104 b. For example, ceramic coating 104 a may be formedof inorganic materials, while the ceramic coating 104 b may be formed oforganic materials. Alternatively, each of the ceramic coatings 104 a,104 b may be formed of different inorganic materials.

An exemplary ceramic coating 104 a is shown in FIG. 3. It should beunderstood that ceramic coating 104 b can also be similarly formed. Afirst coating layer 106 is deposited on the polymeric film 102. Thefirst coating layer 106 may be organic or inorganic in nature. A secondcoating layer 108 then may be deposited on the first coating layer 106.The second coating layer 108 may be organic or inorganic in nature. Inone embodiment, the second coating layer 108 is formed of the samematerial as the first coating layer 106. In one embodiment, the secondcoating layer 108 is formed of the same type of material, i.e., organicor inorganic, as the first coating layer 106 but formed of a differentmaterial of that type. For example, in one embodiment, the first coatinglayer 106 is formed of silicon nitride (SiNx, where x is between about0.6 and 2.0; hereinafter referred to as SiN) and the second coatinglayer 108 is formed of silicon carbide (SiCx, where x is between about1.0 and 2.0; hereinafter referred to as SiC).

A third coating layer 110 may be deposited on the second coating layer108. The third coating layer 110 may be organic or inorganic in nature.In one embodiment, the third coating layer 110 is formed of the samematerial as the first coating layer 106. In one embodiment, the thirdcoating layer 110 is formed of the same material as the second coatinglayer 108. In one embodiment, the third coating layer 110 is formed ofthe same type of material, i.e., organic or inorganic, as the firstcoating layer 106 but formed of a different material of that type. Inone embodiment, the third coating layer 110 is formed of the same typeof material as the second coating layer 108 but formed of a differentmaterial of that type. In one embodiment, the first coating layer 106 isformed of SiN, the second coating layer 108 is formed of SiC, and thethird coating layer 110 is formed of SiN. In one embodiment, the firstand second coating layers 106, 108 are formed of SiN and the thirdcoating layer 110 is formed of SiC. In one embodiment, the first coatinglayer 106 is formed of SiN, the second coating layer 108 is formed ofSiC, and the third coating layer 110 is formed of aluminum oxide(Al₂O₃).

A fourth coating layer 112 may be deposited on the third coating layer110. The fourth coating layer 112 may be organic or inorganic in nature.In one embodiment, the fourth coating layer 112 is formed of the samematerial as the first coating layer 106, the second coating material108, and/or the third coating layer 110. In one embodiment, the thirdcoating layer 110 is formed of the same type of material, i.e., organicor inorganic, as the first, second and/or third coating layers 106, 108,110 but formed of a different material of that type. In one embodiment,the first, second and/or third coating layers 106, 108, 110 are formedof SiN and the fourth coating layer 112 is formed of SiC. In oneembodiment, the first, second and third coating layers 106, 108, 110 areformed of SiN and the fourth coating layer 112 is formed of Al₂O₃. Inone embodiment, the first coating layer 106 is formed of SiC, the secondcoating layer 108 is formed of SiN, the third coating layer 110 isformed of SiC, and the fourth coating layer 112 is formed of Al₂O₃.

It is to be understood that these embodiments are merely exemplary innature and other materials and combinations of materials may be used.For example, it should be understood that the number of coating layersmay be greater or less than the four layers depicted in FIG. 3. Further,inorganic materials may be deposited and gradually tuned to processconditions in which organic materials are then deposited.

The ceramic coatings 104 a, 104 b provide significant improvement inthermal oxidation resistance. Oxygen is a concern in that its presenceaccelerates degradation as well as affects the size of coronadischarges.

The total thickness of the ceramic coatings 104 a, 104 b is determinedupon the composition of the coatings as well as several competingfactors, namely heat resistance and flexibility. The thickness, as wellas the composition, of the ceramic coatings 104 a, 104 b has an effecton the heat resistance provided to the polymeric film 102. Providing agraded composition, i.e., a layer of one or several materials overlyinga second layer of a different material(s), provides greater heatresistance than providing an ungraded composition of coating layers.Specifically, a graded composition improves adhesion between differentmaterials by eliminating hard interfaces therebetween. Further, thethicker the composition, the greater the heat resistance provided.

However, the thicker the composition, the less flexibility that can beexhibited by the coated electrical component without generating excessstress leading to cracking of the ceramic coatings. One embodimentprovides ceramic coatings 104 a, 104 b that are each in the submicron tonanometer range. One embodiment provides only a single ceramic coatinginstead of the paired ceramic coatings 104 a, 104 b.

The ceramic coatings 104 a, 104 b formed on the polymeric film 102 inthe submicron to nanometer range provide a flexible, high heat resistantdielectric shield for protecting electrical components in high voltageand high temperature applications. Through forming a ceramic coating inthe submicron to nanometer thickness range, the hybrid ceramic coatingand polymer structure overcomes thermal oxidation and corona induceddegradation while maintaining film flexibility. Such a structure can beused at temperatures higher than what traditional polymeric materialscan survive, as well as at higher voltages and lower pressures, such asfound in aviation and higher altitude applications. Such a structure canfind utility in various high power density and high voltageapplications, such as, for example, winding and film insulations formotors, transformers, generators, down hole electric motors, powerelectronic boards, and for power and energy capacitors.

Referring now to FIG. 4, there is shown a transmission electronmicroscopy (TEM) image of an insulation separator assembly 100. Theinsulation separator 100 includes a ceramic coating 104 a disposed on amaterial 114 adhered to an epoxy material 116. The material 114 may be,for example, a conductive component. The ceramic coating 104 a has athickness C_(T), which may be in the submicron to nanometer range. Inone embodiment, the thickness C_(T) is between about ten-thousandnanometers and one nanometer. In one embodiment, the thickness C_(T) isbetween about 750 nanometers and 25 nanometers. In one embodiment, thethickness C_(T) is between about 500 nanometers and 50 nanometers. Inone embodiment, the thickness C_(T) is between about 350 nanometers and75 nanometers. In one embodiment, the thickness C_(T) is between about250 nanometers and 100 nanometers. In one embodiment, the thicknessC_(T) is 10 nanometers or less.

With specific reference to FIG. 5, there is shown a deposition system200 for depositing a ceramic coating on a polymeric film 102. Thedeposition system 200 includes a deposition chamber 202, a pair ofspools 210, 212 and a deposition assembly 214 a, 214 b. A gas inletallows for gas to enter the deposition chamber 202 to allow fordeposition of material on the polymeric film 102.

The polymeric film 102 extends from unwinding spool 210 to winding spool212. The spools 210, 212 provide sufficient tension for the polymericfilm 102 as it travels through the deposition chamber 202. Although thespool 210 is termed an unwinding spool and spool 212 is termed a windingspool, it should be understood that the opposite can also be accurate.Furthermore, the spools 210, 212 are configures such that each canrotate in either a clockwise or a counter-clockwise direction. Thus, thespools 210, 212 can move the polymeric film 102 through the depositionchamber 202 in a direction from spool 210 to spool 212 or in an oppositedirection. The ability to change the direction of movement of thepolymeric film 102 allows for multiple layers of the ceramic coating tobe applied to the polymeric film 102 in a continuous manner via aroll-to-roll mechanism. With the change in direction, new material fordeposition can be input into the deposition chamber 202, allowing for agraded composition of ceramic coating on the polymeric film 102.

The deposition system 200 may be configured to allow for the continuousdeposition of material in a suitable fashion. Embodiments of thedeposition system are configured to allow for deposition by way ofchemical-vapor deposition (“CVD”), plasma-enhanced chemical-vapordeposition (“PECVD”), radio-frequency plasma-enhanced chemical-vapordeposition (“RFPECVD”), expanding thermal-plasma chemical-vapordeposition (“ETPCVD”), sputtering, reactive sputtering,electron-cyclotron-resonance plasma-enhanced chemical-vapor deposition(“ECRPECVD”), inductively coupled plasma-enhanced chemical-vapordeposition (“ICPECVD”), an evaporative process, an atomic layerdeposition process, a slurry coating, or combinations thereof.

Referring now to FIG. 6 there is shown a deposition system 300 thatincludes a deposition chamber 302, a pair of spools 210, 212 and adeposition assembly. The deposition chamber 302 includes a firstdeposition chamber 302 separated from a second deposition chamber 308 bya baffle 306. The presence of a pair of deposition chambers 302, 308allows for a graded composition of ceramic material on the polymericfilm in a continuous manner. Further, each of the deposition chambers302, 308 can have different materials being deposited, with the baffle306 preventing significant cross-contamination between depositionchambers.

It should be appreciated that more than two deposition chambers can beincluded within a deposition system. For more information on continuousdeposition of materials on a film-like component, please see U.S. Pat.No. 7,976,899, issue date Jul. 12, 2011 and owned by a common assigneeas the instant patent application. The entire contents of U.S. Pat. No.7,976,899 is incorporated herein by reference.

Referring now to FIG. 7, there is shown a graphical representationexhibiting the thermal stability of a known insulation assembly andinsulation assemblies formed in accordance with an embodiment of theinvention. The thermal gravimetric analysis providing the resultsdisplayed in FIG. 7 is based upon a temperature increase rate of 10°C./minute.

As temperature increases on a material, there will come a point at whichthe material begins to exhibit a heat-related degradation that can bemeasured by percentage of weight lost. Experiments indicate that apercentage of five to 10 weight percent lost in a material used forinsulating a conductive component may lead to a shorting out of thatconductive component. FIG. 7 exhibits thermal gravimetric analyses ofpolymeric film without a coating and polymeric film having a ceramiccoating in accordance with embodiments of the invention. As shown inFIG. 7, in which the temperature change was at a rate of 10° C./minute,the temperature at which about five weight percent has been lost fromthe polymeric film without a coating is about 563° C. The temperature atwhich about 10 weight percent has been lost from the polymeric filmwithout a ceramic coating is about 588° C. The temperature at whichabout five weight percent has been lost from the polymeric film with aceramic coating in FIG. 7 is about 575° C. The temperature at whichabout 10 weight percent has been lost from the polymeric film with aceramic coating is about 600° C.

With specific reference to FIG. 8, and with general reference to FIGS.2-6, next will be described a method of forming a flexible, high heatresistant dielectric shield for protecting electrical components in highvoltage and high temperature applications. At Step 400, at least onelayer of a ceramic material is deposited onto a polymeric film, such aspolymeric film 102. Step 400 may be accomplished in either a batch modeor a continuous mode. In a continuous mode, the polymeric film may beextended between a pair of spools and through a deposition chamber, suchas deposition chambers 200 and/or 300. The polymeric film can betransmitted through the deposition chamber numerous times to obtainmultiple layers of the ceramic coating and to form a graded ceramiccoating composition.

Next, at Step 405 the polymeric film is disposed adjacent to aconducting material. The purpose of disposing adjacent to a conductingmaterial is to provide insulation to the conducting material to inhibitshorting of the conducting material in high temperature environments andapplications. Further, the ceramic coating provides corona dischargeprotection.

While the invention has been described in detail in connection with onlya limited number of embodiments, it should be readily understood thatthe invention is not limited to such disclosed embodiments. Rather, theinvention can be modified to incorporate any number of variations,alterations, substitutions or equivalent arrangements not heretoforedescribed, but which are commensurate with the spirit and scope of theinvention. For example, while embodiments have been described in termsthat may initially connote singularity, it should be appreciated thatmultiple components may be utilized. Additionally, while variousembodiments of the invention have been described, it is to be understoodthat aspects of the invention may include only some of the describedembodiments. Accordingly, the invention is not to be seen as limited bythe foregoing description, but is only limited by the scope of theappended claims.

What is claimed as new and desired to be protected by Letters Patent ofthe United States is:
 1. A high-temperature insulation assembly,comprising: a polymeric film; and at least one ceramic coating disposedon at least one side of the polymeric film, thereby forming thehigh-temperature insulation assembly for use in electrical machines;wherein the high-temperature insulation assembly is disposed onconductive wiring or used as an insulator providing protection againstvoltage hazards or for inhibiting leakage of current, electric dischargeand/or a short circuit current.
 2. The insulation assembly of claim 1,wherein the at least one ceramic coating has a thickness in a rangebetween 1 nanometer and 10,000 nanometers.
 3. The insulation assembly ofclaim 2, wherein the at least one ceramic coating has a thickness in arange between 10 nanometer and 1000 nanometers.
 4. The insulationassembly of claim 1, wherein the ceramic coating is disposed on bothsides of the polymeric film.
 5. The insulation assembly of claim 1,wherein the ceramic coating comprises two or more coatings.
 6. Theinsulation assembly of claim 5, wherein the coatings are at least one ofdifferent materials and different thicknesses.
 7. The insulationassembly of claim 1, wherein the high-temperature insulation assemblyoperates at temperatures above 220 degrees Celsius.
 8. The insulationassembly of claim 1, wherein the polymeric film comprises polyphenyleneoxide, polyphenylene sulfone, polyether sulfone, polyphenylene sulfide,polyimide, aromatic polyimide, aromatic polyester, polyetherimide,polyamideimide, polyetheretherketone, polytetrafluoroethylene,polyvinylidene fluoride, fluorinated ethylene propylene,perfluoroalkoxy, and any combinations thereof.
 9. The insulationassembly of claim 1, wherein the at least one ceramic coating comprisesa pair of ceramic coatings, wherein the polymeric film is sandwichedbetween the pair of the ceramic coatings.
 10. The insulation assembly ofclaim 1, wherein the at least one ceramic coating comprises an inorganicdeposition material.
 11. The insulation assembly of claim 10, whereinthe at least one ceramic coating comprises silicon nitride; siliconoxide; silicon oxynitride; aluminum oxide; zirconium oxide; combinationsof elements of Groups IIA, IIIA, IVA, VA, VIA, VIIA, IB, and IIB; metalsof Groups IIIB, IVB, and VB; rare-earth metals; and, any combinationsthereof.
 12. The insulation assembly of claim 1, wherein the at leastone ceramic coating comprises an organic deposition material.
 13. Theinsulation assembly of claim 12, wherein the at least one ceramiccoating comprises silicon carbide, organometallic silanes, or forms ofceramic coating after sintering.
 14. The insulation assembly of claim 1,wherein the at least one ceramic coating comprises multiple layers ofinorganic deposition material interleaved between multiple layers oforganic deposition material.
 15. An electrical machine, comprising: amotor or generator comprising conductive wiring wound in non-planarorientations; and a high-temperature insulation assembly for insulatingthe conductive wiring and conductive bodies of the motor or thegenerator, said insulation assembly comprising: a polymeric film; atleast one ceramic coating disposed on at least one side of the polymericfilm, thereby forming the high-temperature insulation assembly for usein electrical machines; wherein the high-temperature insulation assemblyis disposed on the conductive wiring or used as an insulator betweenwindings and magnetic materials.
 16. The electrical machine of claim 15,wherein the at least one ceramic coating has a thickness in a rangebetween about 1 nanometer and about 10,000 nanometers.
 17. Theelectrical machine of claim 15, wherein the at least one ceramic coatingcomprises organic materials, inorganic materials, or combinationsthereof.
 18. The electrical machine of claim 17, wherein the at leastone ceramic coating comprises one or more from the group comprisingsilicon nitride, silicon oxide, silicon oxynitride, aluminum oxide,zirconium oxide, silicon carbide, combinations of elements of GroupsIIA, IIIA, IVA, VA, VIA, VIIA, IB, and IIB, metals of Groups IIIB, IVB,and VB, and rare-earth metals, and any combinations thereof.
 19. Theelectrical machine of claim 17, wherein the at least one ceramic coatingcomprises multiple layers of inorganic deposition material interleavedbetween multiple layers of organic deposition material.
 20. A method forforming a high-temperature insulation assembly, comprising: depositingat least one layer of a ceramic material on a polymeric film; anddisposing the at least one layer of a ceramic material and the polymericfilm thereby forming the insulation assembly, wherein the insulationassembly is located proximate a conducting material in an electricalmachine.
 21. The method of claim 20, wherein the at least one ceramiccoating has a thickness in a range between about 1 nanometer and about10,000 nanometers.
 22. The method of claim 20, wherein the at least oneceramic coating comprises organic materials, inorganic materials, orcombinations thereof.
 23. The method of claim 22, wherein the at leastone ceramic coating comprises one or more from the group comprisingsilicon nitride, silicon oxide, silicon oxynitride, aluminum oxide,zirconium oxide, silicon carbide, and any combinations thereof.
 24. Themethod of claim 22, wherein the at least one ceramic coating comprisesmultiple layers of inorganic deposition material interleaved betweenmultiple layers of organic deposition material.
 25. The method of claim20, wherein said depositing comprises chemical-vapor deposition (“CVD”),plasma-enhanced chemical-vapor deposition (“PECVD”), radio-frequencyplasma-enhanced chemical-vapor deposition (“RFPECVD”), expandingthermal-plasma chemical-vapor deposition (“ETPCVD”), sputtering,reactive sputtering, electron-cyclotron-resonance plasma-enhancedchemical-vapor deposition (“ECRPECVD”), inductively coupledplasma-enhanced chemical-vapor deposition (“ICPECVD”), an evaporativeprocess, an atomic layer deposition process, a slurry coating, andcombinations thereof.